S235J2 carbon steel

Low temperature impacting test shall be done for structural steel plate S235J2 under minus 20 centigrade.When rolling of steel plate S235J2,As rolled or Normalizing rolling is both ok.As rolled delivery condition without any special rolling and heat treatment condition.Normalizing rolling process in which the final deformation is carried out in a certain temperature range leading to a material condition equivalent to that obtained after normalizing so that the specified values of the mechanical properties are retained even after noamalizing. Full Data Technical Requirements & Additional Services:
♦ Low temperature impacting test
♦ Rolling under standard NACE MR-0175 (HIC+SSCC)
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user’s demands
Techicals

Mechnical property for S235J2 carbon steel:

Thickness (mm)
S235J2	≤ 16	> 16 ≤ 40	> 40 ≤ 63	> 63 ≤ 80	> 80 ≤ 100	> 100 ≤ 150	> 150 ≤ 200	> 200 ≤ 250	> 250
Yield strength (≥Mpa)	235	225	215	215	215	195	185	175	165
	< 3	≥ 3 ≤ 100				> 100 ≤ 150	> 150 ≤ 250		> 250
Tensile strength (Mpa)	360-510	360-510				350-500	340-490		330-480

Chemical composition for S235J2 mild steel (Ladle Analysis Max%)

Main chemical elements composition of S235J2
Thickness(mm)	C	Si	Mn	P	S	N	Cu
T≤16	0.17	...	1.40	0.025	0.025	...	0.55
16<T≤40	0.17
40<T	0.17